Emebere SS Capillary Tube Seamless iji gbanwee refrigerant mmiri mmiri dị elu ka ọ bụrụ ihe nrịba dị ala nke refrigerant.Ọnụ ego nkwụsị nrụgide ya na-adabere na ogologo na n'ime dayameta nke tube.
304L 6 * 0.5 igwe anaghị agba nchara capillry tubing tubing tubing
316 SS Capillary Tubing bụ ọkọlọtọ molybdenum na-ebu ọkwa ọkwa.Ọ na-enye ihe ndị na-eguzogide corrosion ka mma karịa 304 SS Capillary Tubing, karịsịa nguzogide dị elu na pitting na crevice corrosion na gburugburu chloride.
304L 6 * 0.5 igwe anaghị agba nchara capillry tubing tubing tubing
316 Igwe anaghị agba nchara Capillary Tubing ForHplc bụ ihe mejupụtara ma mmiri mmiri na kọlụm chromatography gas nke a na-eji maka usoro nkwadebe na nyocha n'ofe mpaghara nyocha na biochemistry.
304L 6 * 0.5 igwe anaghị agba nchara capillry tubing tubing tubing
Ngwakọta kemịkalụIgwe anaghị agba nchara 304
Tebụl 1.Ngwakọta kemịkalụ maka 304 igwe anaghị agba nchara alloys
| % | 304 | 304L | 304H |
| C | 0.0 - 0.07 | 0.0-0.03 | 0.04 - 0.08 |
| Mn | 0.0-2.0 | 0.0 - 2.00 | 0.0-2.0 |
| Si | 0.0 - 1.00 | 0.0 - 1.00 | 0.0-1.0 |
| P | 0.0-0.05 | 0.0-0.05 | 0.0 - 0.04 |
| S | 0.0-0.03 | 0.0-0.02 | 0.0-0.02 |
| Cr | 17.50 - 19.50 | 17.50 - 19.50 | 17.00 - 19.00 |
| Ni | 8.00 - 10.50 | 8.00 - 10.50 | 8.00 - 11.00 |
| Fe | Nhazi | Nhazi | Nhazi |
| N | 0.0-0.11 | 0.0-0.11 | 0.0-0.10 |
NjirimaraIgwe anaghị agba nchara 304
Ihe eji arụ ọrụIgwe anaghị agba nchara 304
Tebụl 2a.Ihe eji arụ ọrụ maka alloys igwe anaghị agba nchara 304 - mpempe akwụkwọ ruru 8 mm
| Ọkwa | 304 | 304L | 304H |
| Ike tensile (MPa) | 540-750 | 520-700 | - |
| Ihe mgbakasị ahụ (MPa) | 230 Min | 220 Min | - |
| Elongation A50 mm | 45 min% | 45 min% | - |
Tebụl 2b. Ihe eji arụ ọrụ maka alloys igwe anaghị agba nchara 304 - efere sitere na 8 - 75 mm
| Ọkwa | 304 | 304L | 304H |
| Ike tensile (MPa) | 520-720 | 500-700 | - |
| Ihe mgbakasị ahụ (MPa) | 210 Min | Nkeji 200 | - |
| Elongation A5 | 45 min% | 45 min% | - |
Oge nzipu: Ọgọst-14-2023