Ọkwa 316L/1.4404 Oyi/Na-ekpo ọkụ Rolled igwe anaghị agba nchara eriri igwe/eriri nwere No.1/2B/BA n'elu elu mechaa
| Nkeji edemede | 316L igwe anaghị agba nchara |
| nkọwapụta | Ọkpụrụkpụ (0.3mm-6mm)* Obosara (30mm-1219mm)* Igwe mmiri |
| Elu | Nọmba 1/2B/BA |
| ụdị | igwe igwe |
| Ọkọlọtọ | ASTM JIS EN GB |
| Ojiji | ubi ihe owuwu, ụlọ ọrụ na-ewu ụgbọ mmiri, mmanụ ala, ụlọ ọrụ kemịkalụ, ụlọ ọrụ agha na ọkụ eletrik, nhazi nri na ụlọ ọrụ ahụike, igwe na-ekpo ọkụ ọkụ, igwe na akụrụngwa akụrụngwa. |
| Ịdọba ụgbọala | Ọkọlọtọ mbupụ mbupụ ma ọ bụ dị ka ihe achọrọ/nkwakọ ngwaahịa ahaziri ahazi |
| Ịkwụ ụgwọ | T/T, L/C na anya, Western Union, DP |
316N/316LN igwe anaghị agba nchara chemical mejupụtara
| Ngwakọta kemịkalụ nke igwe anaghị agba nchara 316 | ||||
| Tebụl 1. Ngwakọta kemịkalụ a na-ahụkarị maka 316 igwe anaghị agba nchara | ||||
| % | 316 | 316L | 316H | 316 Ti |
| C | 0.08 | 0-0.03 | 0.04-1 | 0-0.08 |
| Mn | 2.00 | 0-2.0 | 0-2.0 | 0-2.00 |
| Si | 1.00 | 0-1 | 0-1 | 0-1.00 |
| P | 0,045 | 0-0.45 | 0-0.05 | 0=0.045 |
| S | 0.03 | 0-0.03 | 0-0.03 | 0-0.030 |
| Cr | 16.00-18.00 | 10.00-18.00 | 16.00-18.00 | 16.00-18.00 |
| Ni | 10.00-14.00 | 10.00-14.00 | 10.00-14.00 | 10.00-14.00 |
| M0 | 2.00-3.00 | 2.00-3.00 | 2.00-3.00 | TI≥5C |
| Fe | Nhazi | Nhazi | Nhazi | Nhazi |
| Njirimara arụrụ arụ nke igwe anaghị agba nchara 316 | ||||
| Ọkwa | 316 | 316L | 316H/316TI | |
| Ike tensile (N/mm²) | ≥520 | ≥480 | - | |
| Ike mpụta (N/mm²) | 210 | - | - | |
| Ihe mgbakasị ahụ 0.2% (MPa) | 210 | 200 | - | |
| Mgbatị A5 (%) | 40 Min | 40 Min | - | |
| Hardness Rockwell B | 90 | - | - |
Oge nzipu: Feb-11-2023